MASTERS 9000
MASTERS 9000
high temperature acetic sealant
COLOURS
SPECIFICATIONS
- Non-sag
- Immediate adhesion capacity at high and low temperatures ( +5°C / +40°C)
- Flexible at high and low temperatures ( -40°C / +260°C)
- Excellent adhesion on glass, vitrified surfaces, ceramic tiles, various plastic substances and mostly paints
- Maintain elastic property also if it is constantly exposed to +260°C temperature
- Resistance at +275°C for a short time
- Resistance at peaks of +300°C
- Excellent work specifications for professional use
APPLICATIONS
- To stick and seal ovens, fireplaces, boilers and chimney flues
- To seal pumps’ parts, heating systems and household appliances exposed to high temperatures
- Car, industrial and sea engine gaskets
- To seal mechanical parts exposed to high temperatures
PRODUCT DATA
| MASTERS 9000 - Product data | ||||||
|---|---|---|---|---|---|---|
| General characteristics | Inspection method | Unit | Value | |||
| Uncured paste | ||||||
| Density at 23°C | ISO 1183-1 A | [g/cm3] | 1,03 | |||
| Density at 25°C (+/- 0.02 g/cm3) | ISO 1183-1 A | [g/cm3] | 1,03 | |||
| Consistency | ISO 7390, profile U 20 | non-sag | ||||
| Extrusion rate - volume flow at 23°C | [ml/min] | 250 | ||||
| Skin forming time at 23°C / 50 % r.h. | [min] | 20 | ||||
| Cured paste After 4 weeks storage at 23°C / 50% r.h. | ||||||
| Tensile strength | ISO 8339 | [N/mm2] | 0,7 | |||
| Elongation at break | ISO 8339 | [%] | 250 | |||
| Modulus at 100% elongation | ISO 8339 | [N/mm2] | 0,45 | |||
| Hardness - Shore A | ISO 868 | 25 | ||||
| Tear strength | ISO 34, method C | [N/mm] | 4,2 | |||
| Temperature resistance | [°C] | -40 / +260 |
PACKAGE
gas cartridge 200 ml, box 6 pc.
STORAGE
+5 / +25°C – 24 months