MASTERS POLYMER F-104 HT

Glass, mirrors, porcelain and ceramics, rough wood, planed and cork, materials for building industry such as bricks, concrete, plasterboard, to stick plasterboard panels, polyurethane panels, stylofoam and gypsum plaster ceiling roses, stairs covering and counter top, metals like aluminium, painted aluminium, lead, copper, iron and steel
Great adhesion on plastic matters like PVC and polycarbonate

MASTERS POLYMER F-104 HT - Product data

General characteristics	Inspection method	Unit	Value

Uncured paste
Density at 23°C	ISO 2811	[g/cm3]	1,62
Consistency			non-sag
Curing time at 20°C / 45 % r.h.		[mm/24h]	3
Skin forming time at 23°C / 45 % r.h.		[min]	20

Cured paste After 4 weeks storage at 23°C / 50% r.h.
Tensile strength	ISO 37	[N/mm2]	2,10
Elongation at break	ISO 37	[%]	250
Modulus at 100% elongation	ISO 37	[N/mm2]	1,20
Hardness - Shore A	DIN 53505		55
Volume loss		[%]	< -2
Temperature resistance		[°C]	-40 / +100

cartridge 290 ml, box 12/24 pc
drums 260 kg

+5 / +25°C – 24 months