MASTERS POLYMER S-R4
MASTERS POLYMER S-R4
hybrid structural adhesive for wood contructions
COLOURS
SPECIFICATIONS
- Exempt from isocyanates and solvents
- Exempt from phthalates
- Exempt from plasticizers
- Thixotropic non-sag
- One component ready-to-use
- No-stain/ No-halo the surfaces
- Keeps adhesion line
- Workability process similar to polyurethane adhesive
- No-inflating/expansion during reticulation phase
- Excellent filling power
- Great superficial hardness
- Waterproof and more resistant than wood
- Odourless
- Great chromatic stability
- Adhesion properties unchanged over time
- Adhesion without primer
- Excellent extrusion
- Excellent UV resistance: UVB lamp > 4000 h
- Excellent resistance to yellowing
APPLICATIONS
- Wood, MDF, chipboard
- Bonding between wood, metal, stone and concrete
- Structural bonding between different kind of wood
- Bonding of covering on wood, also in humid places
PRODUCT DATA
| MASTERS POLYMER SR-4 - Product data | ||||||
|---|---|---|---|---|---|---|
| General characteristics | Inspection method | Unit | Value | |||
| Uncured paste | ||||||
| Density at 23°C | ISO 2811 | [g/cm3] | 1,30 | |||
| Consistency | non-sag | |||||
| Curing time at 23°C / 50 % r.h. | [mm/24h] | 2 | ||||
| Skin forming time at 23°C / 50 % r.h. | [min] | 35 | ||||
| Cured paste After 4 weeks storage at 23°C / 50% r.h. | ||||||
| Tensile strength | ISO 37 | [N/mm2] | 12,00 | |||
| Elongation at break | ISO 37 | [%] | 30 | |||
| Hardness - Shore A | DIN 53505 | 30 | ||||
| Volume loss | [%] | < -2 | ||||
| Temperature resistance | [°C] | -40 / +120 |
PACKAGE
cartridge 310 ml, box 12/24 pc.
drums 250 kg
STORAGE
+5 / +25°C – 18 months